自动焊锡机烙铁头发黑原因分析

发布时间:2017-08-14 16:44:40   来源:本文转载于网络,由自动焊锡机厂家创盈时代整理,欢迎转载    点击:

随着自动焊锡机的不断在线材行业得到应用,相信广大客户对自动焊锡机的烙铁头也不会感到陌生,自动焊锡机在使用过程中有时候会出现发黑的一些情况,往往很多客户不重视,导致对焊线的效率还是有一定影响的。这是什么原因造成的呢?接下来焊锡机厂家技术人员为你详细解答自动焊锡机烙铁头发黑的原因。

With the development of automatic soldering machine has been applied in the wire industry, believe that the majority of customers of the automatic soldering machine welding head will not feel strange, automatic soldering machine in use process sometimes appear black in some cases, often ignored of a lot of customers, lead to the efficiency of butt welding line or have a certain influence. What causes it? Next, the technician of the soldering machine factory will give you a detailed explanation of the black reason of the soldering iron hair.  

1、有铅锡线:使用有铅的锡线和无铅的烙铁头会缩短烙铁头的寿命,加速烙铁头的氧化,也会出现烙铁头发黑。

1. Lead tin line: using lead tin and lead-free soldering iron head will shorten the life of the soldering iron head, accelerate the oxidation of the iron head, and the iron hair will be black.   

2、长时间使用,即使不使用助焊剂也会发黑的,烙铁头的寿命一般都不高,长时间的使用寿命结束将会变黑。

2. Long time use, even if the use of the flux can be dark, the life of the soldering iron head is generally not high, and the long service life will be blackened.    

3、烙铁头发黑是氧化反应,和助焊剂有直接关系。一般的助焊剂带酸性,会加剧氧化。

3. Soldering iron hair black is oxidation reaction, and the flux has direct relation. Generally, the flux is acidic and will increase oxidation.

自动焊锡机   
 

4、氧化,与温度关系大,温度越高氧化越快。

4. Oxidation, with great temperature, the higher the temperature, the faster the oxidation.    

5、锡的原因,锡在氧化后是黑色的,古代的铜镜有锡、铜、锌之类的成份,就是利用了这些东西氧化后用它们的氧化物来磨镜子的表面使之光亮的。

5, tin, tin is black after oxidation, ancient bronze mirror with ingredients such as tin, copper, zinc, is the use of these things after oxidation with their oxides to grind the surface of the mirror polished.    

以上就是自动焊锡机烙铁头发黑原因分析的一些介绍,相信大家对自动焊锡烙铁头发黑也有了一定的了解,自动焊锡机发黑的原因有很多,通常自动焊锡机恒温焊台长时间没有调试,在不恒温的状态下使用烙铁头,自动焊锡机烙铁头就会出现发热、发红、然后变黑。所以在平时的工作中不仅要保养烙铁头也要做好恒温焊台的养护。

Above is automatic soldering machine soldering iron hair black cause analysis some introduction, believe everybody for automatic soldering iron hair black also had certain understanding, automatic soldering machine nigrescent reason has a lot of, usually automatic soldering machine constant temperature welding head time no debugging, without use soldering iron head under the condition of constant temperature, automatic soldering machine welding head can appear fever, redness, and black. So in the ordinary work not only to maintain the soldering iron head should also do the maintenance of the thermostatic welding table. 

深圳市创盈时代科技是荣获国家高新技术企业称号的自动焊锡机厂家,专注于双Y双头焊锡机、双头三头焊锡机、三轴四轴焊锡机、焊锡设备整体解决方案领导者,为你提供整体点胶解方案,欢迎来电咨询。

原文地址:http://www.chytime.com/news/hxjs/1646.html

本文关键字:自动焊锡机烙铁头发黑原因分析

本文由www.chytime.com 深圳创盈时代科技有限公司 自动点胶机整理,欢迎转载,转载时请标明出处。

上一篇:自动焊锡机的焊接作业的有哪些特征和特点
下一篇:点胶机的应用领域汇总